Abstract: This paper analyzed the statistical data of RAPEX notification on chemical risks in 2012, and illustrated separately on chemical notifications involved in product category, type of hazardous substance, notifying country and country of original, etc. Meanwhile, the paper also summarized the …
3/15/2013 11:41:00 AM
Abstract: A new pigment padding process was explored on the basis of modified CVC fabric treated by selfmade cationic modification agent. The dosages of adhesive and crosslinking agent, the curing temperature and time were optimized to obtain higher K /S value and color fastness to washing and rubbin…
3/15/2013 11:40:00 AM
Abstract: A new modifier was synthesized using epoxy chloropropane and sericin protein, and then applied to the modification of cotton fabrics. FT-IR and SEM were used to characterize the modification effect, and the results showed that sericin protein had fixed on cotton fabrics. Reactive dyes were …
3/15/2013 11:39:00 AM
Abstract: Silver ammonia complexion was reduced by cyclodextrins hydrolysate to get nano-silver solution.The size and size distribution of nano-silver were measured by HPPS and TEM. Then the solution was used to treat cotton fabrics, and the antibacterial performance of treated fabrics was investigat…
2/21/2013 2:32:00 PM
Abstract: Spectrophotometer can provide a convenient way to test the concentration of nano-sliver solution, so it is used to analyze the adsorption properties and related mechanism of nano-silver solution onto viscose fiber. In this paper, the influence of concentration of nano-silver solution, dippi…
2/21/2013 1:59:00 PM
Abstract: In this paper the process of digital printing using the reactive dye ink on grain leather was studied. In order to solve the problem of poor rubbing fastness, different reagents were used on leather respectively before printing. When the leather was overprinted with the modifier G after dig…
2/21/2013 1:52:00 PM
Abstract: Silver nanoparticle colloid was prepared through the reduction of silver nitrate by modified hyperbranched polymer (MHBP) in aqueous solution. The generated silver nanoparticles were characterized by UV-Vis, XRD, Nano-Sizer and TEM. The diameter of silver nanoparticle was around 10 nm and c…
1/11/2013 2:00:00 PM
Abstract: Nano-silver solution was prepared by maltose. The size and distribution of maltose nanoparticles were tested with HPPS and TEM. After cotton fabrics were finished with maltose nanoparticles, whiteness, antibacterial efficacy and washing durability of the fabrics were studied. The results sh…
1/11/2013 1:59:00 PM
Abstract: To overcome the shortage of traditional pigment dyeing, CVC fabric was modified by self-made cationic modifier HL. K/S value, dry/wet rubbing fastness and washing fastness were tested to evaluate dyeing effect, and the optimized modified conditions were defined as follow: modifier HL 10 g/L…
1/11/2013 1:58:00 PM
Abstract: Two nano-sized titania systems were prepared by a sol-gel method and a surface modification method, respectively. Surface morphology, light fastness, and color change of dyed PET fabric treated with those systems were compared. Result shows that surface morphology of titania on the fibers t…